Grade/Product Name: P-SF-060
“P-SF-060” is a polypropylene homo-polymer with good flow properties and particularly suitable for the extrusion of film yarn, monofilament, cast film and sheet. combines outstanding processability with good mechanical properties .film yarn of P-SF-060 , is used for baler twines , packaging twines and ropes.
“P-SF-060” is well suited for the production of monofilament used for instance in brush and broom filling and technical applications.
“P-SF-060” is suitable for the production in film yarn industry for bags & heavy duty jumbo bag.
Processing Method:Extrusion (film yarn, monofilament) -sheet-cast film
good mechanical properties
Typical Applications:production in film yarn industry for bags & heavy duty jumbo bag
Baler twines, packaging twines and ropes. Thin sheet for stationery folders.
Sheet for thermoforming
Brush and broom filling and technical applications.
parts for automotive industry, toys and the garden furniture
|Melt flow rate(230° c/2.16 kg)||6.0||dg/min||ASTM D 1238|
|Density||0.9||g/cm3||ASTM D 1505|
|Flexural Modulus||1500||MPa||ASTM D790|
|Tensile Strength at Yield||35||MPa||ASTM D 638|
|Tensile Elongation at Yield||12||%||ASTM D 638|
|Izod cImpactStrength(notched)at23° c||30||J/m||ASTM D256|
|Vicat softening point (10 N)||154||°c||ASTM D 1525|
|H.D.T (0.46 MPa)||94||°c||ASTM D 648|
Grade/Product Name: ZR340R
ZR340R offers a very good flowability and an excellent transparency and organoleptic performance. ZR340Ris typically used in the production of thin walled packaging with high transparency and high requirements for organoleptic properties.
Processing Method:Injection molding
Injection stretch blow molding
Typical Applications:Household containers, housewares
Packaging for food, cosmetics and pharmaceutical products
Clear tubs and pots for ice cream, yoghurt and other desserts
Medical sector such as syringes, test tubes and vials
Lids, caps and closures
CD and DVD boxes
Injection stretch blow molded containers and bottles
Sports, leisure and toys
|Melt Flow Rate (230°C, 2.16kg)||g/10min||25||± 3||ASTM D1238|
|Flexural Modulus||MPa||1050||± 100||ASTM D790|
|Tensile Strength at Yield||MPa||28||± 4||ASTM D638|
|Tensile Elongation at Yield||%||13||± 3||ASTM D638|
|Izodimpact strength (notched) at 23°C||J/m||>100||-||ASTM D256|
|Rockwell Hardness||R-Scale||94||± 10||ASTM D785|
|Vicat softening point||°C||125||± 5||ASTM D1525|
|H.D.T. (0.45 MPa)||°C||83||± 8||ASTM D648|
|Haze (1 mm)||%||15||± 3||ASTM D1003|
|Gloss||-||75||± 8||ASTM D2457|